Intrinsic factors of bearing temperature are:
1) cavities in ceramic media: the main factors leading to the formation of voids are organic or inorganic pollution in ceramic powder, improper control of sintering process, etc.
2) the main reason is related to the cooling rate during sintering, and the crack and harm are similar to the cavity.
3) delamination: the sintering of multilayer ceramic capacitors is stacked and co-fired. The sintering temperature can be as high as 1000 ℃. The interlaminar adhesion is not strong, the internal pollutant volatilization during the sintering process, and the improper control of the sintering process may lead to the stratification.
The main external factors are:
1) the temperature impact crack is mainly caused by the impact of the device during the welding, especially the wave peak welding, and improper rework is also the important cause of the temperature impact crack.
Analyze the development status of metallized film capacitors
The structure and characteristics of polypropylene film capacitors
How to prevent film capacitor failure? What issues should be paid attention to?
Why does the CBB film capacitor visibly heat up when it operates?
A brief overview of the requirements for the film capacitors selection
Analysis on the self-healing characteristics of film capacitors
The advantages and technical requirements of metallized polypropylene film capacitors
A brief description of the five applications commonly used in CBB capacitors